Highly dispersive nanospheres of MnFe204 are prepared by template free hydrothermal method. The nanospheres have 47.3-nm average diameter, narrow size distribution, and good crystallinity with average crystallite size about 22 nm. The reaction temperature strongly affects the morphology, and high temperature is found to be responsible for growth of uniform nanospheres. Raman spectroscopy reveals high purity of prepared nanospheres. High saturation magnetization （78.3 emu/g）, low coercivity （45 Oe, 10e = 79.5775 A.cm-1）, low remanence （5.32 emu/g）, and high anisotropy constant 2.84 × 10^4 J/m3 （10 times larger than bulk） are observed at room temperatures. The nearly snperparamagnetic behavior is ~ spin due to comparable size of nanospheres with superparamagnetic critical thameter Dcr spm The high value of Keff may be due to coupling between the pinned moment in the amorphous shell and the magnetic moment in the core of the nanospheres. The nanospheres show prominent optical absorption in the visible region, and the indirect band gap is estimated to be 0.98 eV from the transmission spectrum. The prepared Mn ferrite has potential applications in biomedicine and photocatalysis.
The interaction and its variation between magnetic grains in two kinds of magnetic recording tapes are investigated by first-order reversal curves （FORC） and the 5M method. The composition and microstructure of the samples are characterised by x-ray diffraction and scanning electron microscope. The FORC diagram can provide more accurate information of the interaction and its variation, but the 5M curves cannot. The positive interaction field and the large variation of the interaction field have opposite effects on the δM curve.