Light weight and mechanically strong α-chitin aerogels were fabricated using the sol-gel/self-assembly method from α-chitin in different aqueous alkali hydroxide(KOH, Na OH and Li OH)/urea solutions. All of the α-chitin solutions exhibited temperature-induced rapid gelation behavior. 13 C nuclear magnetic resonance(NMR) spectra revealed that the aqueous alkali hydroxide/urea solutions are non-derivatizing solvents for α-chitin. Fourier transform infrared(FT-IR), X-ray diffraction(XRD) and cross-polarization magic angle spinning(CP/MAS) 13 C NMR confirmed that α-chitin has a stable aggregate structure after undergoing dissolution and regeneration. Subsequently, nanostructured α-chitin aerogels were fabricated by regeneration from the chitin solutions in ethanol and then freeze-drying from t-Bu OH. These α-chitin aerogels exhibited high porosity(87% to 94%), low density(0.09 to 0.19 g/cm^3), high specific surface area(419 to 535 m^2/g) and large pore volume(2.7 to 3.8 cm^3/g). Moreover, the α-chitin aerogels exhibited good mechanical properties under compression and tension models. In vitro studies showed that m BMSCs cultured on chitin hydrogels have good biocompatibility. These nanostructured α-chitin aerogels may be useful for various applications, such as catalyst supports, carbon aerogel precursors and biomedical materials.
Beibei DingDan ZhaoJianhui SongHuichang GaoDuoduo XuMin XuXiaodong CaoLina ZhangJie Cai