Solidification of Fe-7.5%Mo-16.5%Si ternary quasiperitectic alloy is investigated by using differential scanning calorimetry (DSC) and drop tube containerless processing techniques.The primary phase is identified as R (Fe5Mo3Si2) and the quasiperitectic phases are τ1 (Fe5MoSi4) and Fe3Si.With the decrease of droplet diameter, the cooling rate and undercooling of the droplets in-crease rapidly.The experiment result indicates that the solidification microstructure is composed of remnant primary phase, qua-siperitectic phases and ternary eutectic when the droplet diameter exceeds 400 μm, whereas the ternary eutectic is suppressed when the droplet is smaller than 400 μm in diameter.