A new coordination polymer [Cd2(5-IPA)(HL)2(H2O)2]·4H2O(1) was prepared under hydrothermal conditions based on 5-hydroxy-isophthalic acid(5-H2IPA) with multi-N-donor ligand 1-(1H-imidazol-4-yl)-3-(4H-tetrazol-5-yl)benzene(H2L). The complex was characterized by IR spectroscopy, TGA, X-ray powder and single-crystal diffraction. It crystallizes in the monoclinic system, space group C2/c with a = 23.6291(18), b = 9.9847(8), c = 17.7244(14) ?, β = 124.6180(10)?, V = 3441.4(5) ?3, Z = 4, C28H30N12O11Cd2, Mr = 935.44, Dc = 1.805 g/cm3, μ = 1.313 mm-1, S = 1.055, F(000) = 1864, the final R = 0.049 and w R = 0.1315 for 2985 observed reflections(I > 2σ(I)). The central metal Cd(II) atoms with octahedral coordination geometry are six-coordinated by three oxygen and three nitrogen atoms. The HL- ligands from the deprotonated H2 L connect Cd(II) atoms to form two-dimensional(2D) double-layer fes networks which are further pillared by 5-IPA2- ligands into a rare binodal(3, 4)-connected three-dimensional(3D) architecture with a(4·6·8)(4·62·83) fsc-3,4-C2/c topology. Solid state luminescent property and sorption property of 1 have been investigated.
A new complex, [Ni2(L)4(H2O)8](1, L1 = 4-(1H-imidazol-4-yl)benzoic acid), has been hydrothermally prepared and characterized by single-crystal X-ray diffraction, IR spectroscopy, elemental analysis and PXRD. Complex 1 crystallizes in monoclinic, space group P21/c with a = 22.281(2), b = 7.3959(7), c = 24.978(3) ?, β = 90.876(10), V = 4115.6(7) ?3, Z = 8, C20H22N4O8Ni, Mr = 505.13, Dc = 1.630 g/cm3, μ = 1.001 mm-1, S = 1.080, F(000) = 2096, the final R = 0.452 and wR = 0.1152 for 9380 observed reflections(I > 2σ(I)). The result of X-ray diffraction analysis revealed three different kinds of Ni(II) centre mononuclear molecules in the asymmetric unit. The independent mononuclear units are bridged to form a three-dimensional supramolecular polymer by extensive hydrogen bonds and C–H···π non-covalent bonding interactions.
A novel complex, [Zn(L)]2·H2O(1, H2 L = 4-aminophthalic acid), has been hydrothermally prepared and characterized by single-crystal X-ray diffraction, IR spectroscopy, elemental analysis and PXRD. Complex 1 crystallizes in monoclinic, space group C2/c with a = 12.4267(6), b = 7.7482(3), c = 18.6983(8) ?, β = 110.437(3)o, V = 1687.04(13) ?3, Z = 4, C16H12N2O9Zn2, Mr = 507.06, Dc = 1.996 g/cm3, μ = 2.903 mm-1, S = 0.989, F(000) = 1016, the final R = 0.0304 and w R = 0.0720 for 12618 observed reflections(I > 2σ(I)). Single-crystal X-ray structural analysis reveals that compound 1 features a three-dimensional(3D) framework with 4-connected umc topology. Moreover, the thermogravimetric(TG) analysis and photoluminescent property of 1 were also discussed.