The aim of this work was to investigate the effects of calcination/acid-activation on the composition, structure, and photocatalytic (PC) reduction property of an anodic oxidation TiO2/Ti film catalyst. The surface morphology and phase composition were examined by scanning electron microscopy and X-ray diffraction. The catalytic property of the film catalysts was evaluated through the removal rate of potassium chromate during the PC reduction process. The results showed that the film catalysts were composed of anatase and rutile TiO2 with a micro-porous surface structure. The calcination treatment increased the content of TiO2 in the film, changed the relative ratio of anatase and rutile TiO2, and decreased the size of the micro pores of the film catalysts. The removal rate of potassium chromate was related to the technique parameters of calcination/acid-activation treatment. When the anodic oxidation TiO2/Ti film catalyst was calcined at 873 K for 30 min and then acid-activated in the concentrated H2SO4 for 60 min, it presented the highest catalytic property, with the removal rate of potassium chromate of 96.3% during the PC reduction process under the experimental conditions.
YAO ZhongpingJIANG YanliJIANG ZhaohuaZHU HongkuiBAI Xuefeng