Low density polyethylene(LDPE)/lignin blends were prepared using melt blending.Two kinds of compatibilizers, ethylene-vinylacetate(EVA) which is softer than LDPE and polyethylene grafted with maleic anhydride(PE-g-MA) which is harder than LDPE were used to improve the interfacial adhesion.Scanning electron microscope(SEM) was used to investigate the dispersion of lignin in LDPE matrix.The results showed that both of the compatibilizers could improve the interaction between the low density polyethylene an...
Double melting behavior of poly(trimethylene terephthalate) (PTT) was studied in detail by means of differential scanning calorimetry (DSC) and optical microscopy. The results indicate that the low-temperature melting peak of PTT at ca. 218℃ for the samples crystallized isothermally at 203℃ is associated with the melting of crystals produced by secondary crystallization, while the high-temperature melting peak of it at about 227℃ is related to the melting of the crystals produced by primary crystallization. The results further demonstrate that the PTT crystals growing non-isothermally during cooling process are thermodynamically unstable and can undergo structure reorganization during the DSC heating scan. The reorganized crystals melt at temperature higher than the crystals produced by secondary crystallization at 203 ℃. Consequently, for the non-fully crystallized samples, the crystals grown during cooling also exhibit contribution to the high-temperature melting peak.