Polyethylene terephthalate mesh（PET） enhanced cellulose acetate membranes were fabricated via a phase inversion process. The membrane fabrication parameters that may affect the membrane performance were systematically evaluated including the concentration and temperature of the casting polymer solution and the temperature and time of the evaporation, coagulation and annealing processes. The water permeability and reverse salt flux were measured in forward osmosis（FO） mode for determination of the optimal membrane fabrication conditions. The optimal FO membrane shows a typical asymmetric sandwich structure with a mean thickness of about 148.2 μm. The performance of the optimal FO membrane was tested using 0.2 mol/L Na Cl as the feed solution and 1.5 mol/L glucose as the draw solution. The membrane displayed a water flux of 3.47 L/（m2·hr） and salt rejection of95.48% in FO mode. While in pressure retarded osmosis（PRO） mode, the water flux was4.74 L/（m2·hr） and salt rejection 96.03%. The high ratio of water flux in FO mode to that in PRO mode indicates that the fabricated membrane has a lower degree of internal concentration polarization than comparable membranes.
Four common types of additives for polymer membrane preparation including organic macromolecule and micromolecule additives, inorganic salts and acids, and the strong non-solvent H2 O were used to prepare poly（vinylidene fluoride-co-chlorotrifluoroethylene）（PVDF-CTFE） hydrophobic flat-sheet membranes. Membrane properties including morphology, porosity, hydrophobicity, pore size and pore distribution were investigated, and the permeability was evaluated via direct contact membrane distillation（DCMD） of 3.5 g/L Na Cl solution in a DCMD configuration. Both inorganic and organic micromolecule additives were found to slightly influence membrane hydrophobicity. Polyethylene glycol（PEG）,organic acids, Li Cl, Mg Cl2, and Li Cl/H2 O mixtures were proved to be effective additives to PVDF-CTFE membranes due to their pore-controlling effects and the capacity to improve the properties and performance of the resultant membranes. The occurrence of a pre-gelation process showed that when organic and inorganic micromolecules were added to PVDF-CTFE solution, the resultant membranes presented a high interconnectivity structure. The membrane prepared with dibutyl phthalate（DBP） showed a nonporous surface and symmetrical cross-section. When H2 O and Li Cl/H2 O mixtures were also used as additives, they were beneficial for solid–liquid demixing, especially when Li Cl/H2 O mixed additives were used. The membrane prepared with 5% Li Cl ＋ 2% H2 O achieved a flux of24.53 kg/（m2·hr） with 99.98% salt rejection. This study is expected to offer a reference not only for PVDF-CTFE membrane preparation but also for other polymer membranes.
Libing ZhengZhenjun WuYong ZhangYuansong WeiJun Wang