Cathodic protection is a very effective method to protect metals, which can form calcareous deposits on metal surface. Research on the interrelationship between fouling organism and calcareous deposits is very important but very limited, especially sulfate-reducing bacteria(SRB). SRB is a kind of very important fouling organism that causes microbial corrosion of metals. A study of the influence of calcareous deposit on corrosion behavior of Q235 carbon steel in SRB-containing culture medium was carried out using electrochemical impedance spectroscopy(EIS), scanning electron microscopy(SEM) and surface spectroscopy(EDS). The calcareous deposit was formed with good crystallinity and smooth surface under the gradient current density of -30 μA cm^(-2) in natural seawater for 72 h. Our results can help elucidate the formation of calcareous deposits and reveal the interrelationship between SRB and calcareous deposits under cathodic protection. The results indicate that the corrosion tendency of carbon steel was obviously affected by Sulfate-reducing Bacteria(SRB) metabolic activity and the calcareous deposit formed on the surface of carbon steel under cathodic protection was favourable to reduce the corrosion rate. Calcareous deposits can promote bacterial adhesion before biofilm formation. The results revealed the interaction between biofouling and calcareous deposits, and the anti-corrosion ability was enhanced by a kind of inorganic and organic composite membranes formed by biofilm and calcareous deposits.
Research on corrosion behaviour of zinc in natural sea water without and with fucoidan was carried out by potentiodynamic polarisation test and electrochemical impedance spectroscopy(EIS). The results revealed that fucoidan serves as a good inhibitor for zinc in sea water. Polarisation curves suggested that corrosion potential values shifted to the positive ones after adding inhibitor and fucoidan retards anodic reaction more. Thus, fucoidan can be acted as anodic inhibitor. EIS results showed two phenomena including a charge transfer and an adsorption film. The corrosion inhibition of fucoidan was further confirmed by the scanning electron microscope(SEM) and atomic force microscope(AFM)analysis. Langmuir's adsorption isotherm was found the appropriate adsorption model.
Cui WangJie ZhangXiao-Lin ChenBin XiangJi-Zhou DuanBao-Rong Hou