Using Ti as the super-resolution reflective film to replace the A1 reflective layer in conventional read-onlyoptical disk, the recording marks with a diameter of 380 nm and a depth of 50 nm are read out in adynamic testing device whose laser wavelength is 632.8 nm and numerical aperture of the lens is 0.40. Theoptimum Ti thin film thickness is 18 nm and the corresponding signal-noise-ratio is 32 dB.
A novel symmetrical charge transfer fluorene-based compound 2,7-bis (4-methoxystyryl)-9, 9-bis (2-ethylhexyl)-9H-fluorene (abbreviated as BMOSF) was synthesized and its nonlinear absorption was investigated using two different laser systems: a 140-fs, 800-nm Ti:sapphire laser operating at 1-kHz repetition rate and a 38-ps, 1064-nm Nd:YAG pulsed laser operating at 10-Hz repetition rate, respectively. Unique nonlinear absorption properties in this new compound were observed that rise from multiphoton absorption. The nonlinear absorption coefficients were measured to be 6.02 × 10-3 cm/GW (due to two-photon absorption, exciting wavelength is 800 nm) and 3.6×10-20 cm3/W2 (due to three-photon absorption, exciting wavelength is 1064 nm). This new compound possesses strong fluorescence induced by two-photon absorption and obvious three-photon absorption optical limiting effects.
The optical absorption properties of phase-change optical recording thin films subjected to various initialization conditions were investigated. The effects of initialization power and velocity on optical constants of the Ge2Sb2Te5thin films were also studied. The energy gap of Ge2Sb2Te5 thin films subjected to various initialization conditions was also obtained. It was found that the optical energy gap of the Ge2Sb2Te5 thin films increased with either increasing initialization laser power or decreasing initialization velocity, with peak of 0.908 eV at laser power of 1000 mW or initialization velocity of 4.0 m/s, but the continued increasing initialization laser power or decreasing initialization velocity resulted in the decrease of the optical energy gap. The change of the optical energy gap was discussed on the basis of amorphous crystalline transformation.
Ming FANG, Qinghui LI and Fuxi GANShanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, Shanghai 201800, China