A 1.55μm Fabry-Perot (F-P) thermo-optical t unable filter is fabricated.The cavity is made of amorphous silicon (a-Si) layer grown by electron-beam evaporation technique.Due to the excellent thermo-optical property of a-Si,the refractive index of the F-P cavity will be changed by heating;the transmittance resonant peak will therefore shift substantially.The measured tuning rang is 12nm, FWHM (full-width-at-half-maximum) of the transmissi on peak is 9nm,and heating efficiency is 0.1K/mW.The large FWHM is mainly due to th e non-ideal coating deposition and mirror undulation.Possible improvements to increase the efficiency of heating are suggested.
A SiGe/Si multi-quantum wells resonant-cavity-enhanced(RCE) detector with high reflectivity bottom mirror is fabricated by a new method.The bottom mirror is deposited in the hole,which is etched from the backside of the sample by ethylenediamine-pyrocatechol-water(EPW) solution with the buried SiO 2 layer in SOI substrate as the etching-stop layer.Reflectivity spectrum indicates that the mirror deposited in the hole has a reflectivity as high as 99% in the range of 1.2～1.5μm.The peak responsivity of the RCE detector at 1.344μm is 1.2mA/W and the full width at half maximum is 12nm.Compared with the conventional p-i-n photodetector,the responsivity of RCE detector is enhanced 8 times.