A crossed molecular beams, state-to-state scattering study was carried out on the F＋H2→HF＋H reaction at the collision energy of 5.02 kJ/mol, using the highly sensitive H atom Rydberg tagging time-of-flight method. All the peaks in the TOF spectra can be clearly assigned to the ro-vibrational structures of the HF product. The forward scattering of the HF product at v′=3 has been observed. The small forward scattering of the HF product at v′=2 has also been detected. Detailed theoretical analysis is required in order to fully understand the dynamical origin of these forward scattering products at this high collision energy.
为了评估材料的抗原子氧腐蚀能力,首先在地面模拟设备上通过激光爆破法产生平动能约为4.5 e V的原子氧束源,然后利用此高能氧束源对苯基硅橡胶热控涂层材料进行暴露实验。材料受高能原子氧轰击而导致的影响,分别通过质量、X射线光电子能谱和扫描电镜进行表征。结果显示,原子氧累积通量9.5×10^(19)atoms/cm^2及8.5×10^(20)atoms/cm^2暴露实验后,材料表面微观形貌没有明显腐蚀,质量有少许增加,表面化学组成发生明显变化,分析认为是形成非挥发性物质SiO_x。实验结果表明,苯基硅橡胶热控涂层材料具有优越的抗原子氧腐蚀能力,推测其机理是形成的SiO_x钝化层作为保护层对其下方的材料进行保护,阻止原子氧对材料进一步腐蚀。