The hot cracking of the continuous casting bullit is connected with its macrostructure and mechanical property burnt. The macrostructure and the mechanical property of 0. 13 wt- %C continuous casting bullit was investigated. The results are as follows: 1) the classical representation of the casting bullit shows three distinct zones, a peripherial region of small equiaxed grains, a columnar zone, and a central equiaxed zone. The rapid increase of the under cooling layer thickness is the criterion of the transformation from the columnar zone to central equiaxed zone; 2) The hardness decreases with the reducing of the solidification speed; 3) The tensile strength decreases gradually from the peripherial equiaxed maximum principal strain zone to central equiaxed zone ,and increases with the drop of the temperature.